Equipped with modernized Wet Lab facilities and latest German technology Spectrometer through which strict quality control measures are practiced to achieve the specified product quality standards. The spectro lab determines the physical and chemical composition of the steel bars.

Two hydraulic controlled Universal Tensile Testing Machines conduct a stress test on the steel bar, and gives readings of the proof test, tensile stress and elongation ensuring that the rebars manufactured at our facility conform to the strictest quality standards

Quality Control Labs

mechanical-lab
– Universal testing machine 2000 KN.
– Universal testing machine 100 KN.
– Rockwel hardness tester.
– Portable hardness tester.

wet-analysis-lab

– SPECTRO LAB M-11
– SPECTRO MAXX LMF16

spectro-lab

– Muffle Furnace
– Electric Oven
– Analytical balance
– Water Distillation Plant
– Fume hood
– Hot Plate

Quality Assurance Standards

BILLETS STANDARD
Chemical Composition C % Si % Mn % P % S % C.E
GRADE
ASTM G-60 0.28-0.32 0.17-0.35 1.20-1.40 0.04 0.04 <0.55
SWRM 6/1006 0.08 0.15 0.4 0.04 0.04
SWRM 8/1008 0.10 0.15 0.6 0.04 0.04
ASTM-A615 G-60
Chemical Composition C % Si % Mn % P % S % C.E
0.28-0.32 0.17-0.35 1.20-1.40 0.04 0.04 0.55
Mechanical Properties YIELD STRENGTH TENSILE STRENGTH ELONGATION %
Mpa Psi Mpa Psi (10-19mm) (22-25mm)& (29-57mm)
420 60,000 620 90,000 9 8 & 7
BS4449 G-550
Chemical Composition C % Si % Mn % P % S % C.E
0.18-0.24 0.15-0.30 0.60-0.90 0.045 0.045
Mechanical Properties YIELD STRENGTH TENSILE STRENGTH ELONGATION
Mpa Psi Mpa Psi %
550 79750 575 83375 14
Wire Rod
Chemical Composition C % Si % Mn % P % S %
0.08 0.15 0.4 0.04 0.04
Mechanical Properties YIELD STRENGTH TENSILE STRENGTH ELONGATION
Mpa Psi Mpa Psi %
420 Max 60,900 25
Chemical Composition C % Si % Mn % P % S %
0.10 0.15 0.6 0.04 0.04
Mechanical Properties YIELD STRENGTH TENSILE STRENGTH ELONGATION
Mpa Psi Mpa Psi %
440Max 63,800 22
Chemical Composition C % Si % Mn % P % S %
0.20-0.25 0.25 0.30-0.60 0.04 0.04
Mechanical Properties YIELD STRENGTH TENSILE STRENGTH ELONGATION
Mpa Psi Mpa Psi %
600Max 87000 22